10-11mm Pressureless Sintered Silicon Carbide Grinding Balls
製品詳細
Pressureless Sintered Silicon Carbide Grinding Balls
,11mm Silicon Carbide Grinding Balls
Pressureless sintered silicon carbide (SiC) grinding balls are precision ceramic grinding media manufactured by sintering nano- or submicron SiC powders in a non-oxidising atmosphere at high temperatures. The 10–11 mm size falls into the optimal range for drum (rolling) ball mills, offering an excellent combination of high hardness and moderate density.
Key Size Applications:
- 0.5–2 mm: Ultra-fine grinding of extremely hard materials
- 2–8 mm: Preferred media for stirred mills
- 8–15 mm: Specifically designed for drum ball mills
Pressureless sintering involves submicron β-SiC powder with sintering aids (0.3–3.0 wt% boron and 0.1–1.0 wt% carbon), sintered at 2020–2080°C in inert atmosphere. For 10–11 mm balls, cold isostatic pressing (CIP) is used to create spherical blanks, which are then precision-machined and sintered to ensure high sphericity and uniform density.
| Parameter | Value / Range | Unit |
|---|---|---|
| True Density | >3.15 | g/cm³ |
| Hardness (Vickers) | 2000–2500 | HV |
| Bending Strength | 360–470 | MPa |
| Compressive Strength | >2200 | MPa |
| Fracture Toughness | 3.0–5.12 | MPa·m¹⁄² |
| Elastic Modulus | 350–380 | GPa |
| Max. Operating Temperature | 1600 | °C |
| Thermal Conductivity | 95–120 | W/m·K |
| Property | Pressureless Sintered SiC | ZrO₂ | Al₂O₃ | Steel |
|---|---|---|---|---|
| Density (g/cm³) | >3.15 | ≈6.0 | ≈3.95 | ≈7.8 |
| Vickers Hardness (HV) | 2000–2500 | 1100–1300 | ≈1800 | ≈700 |
| Max. Operating Temp. (°C) | 1600 | 400 | 1000 | ~300 |
| Fracture Toughness (MPa·m¹⁄²) | 3.0–5.12 | 8.0–10.0 | 3.0–4.0 | — |
- Superhard material grinding: SiC, B₄C, TiC, Si₃N₄, diamond
- Mining & metallurgy: Hard ores like quartz and corundum
- Electronic & structural ceramics: Non-magnetic and electrically insulating
- Chemical & corrosive environments: Stable in strong acids and alkalis
- New energy & semiconductor materials: High-purity battery and substrate materials
| Consideration | Recommendation |
|---|---|
| Equipment Match | Drum (rolling) ball mills |
| Material to be Ground | Hard powders (Mohs ≥7) |
| Purity Requirements | Products requiring ≥99.5% purity |
| Impact Severity | Avoid extremely high impact conditions |
| Operating Temperature | Room temperature up to 1300°C |
Important Note: Although SiC is extremely hard, its fracture toughness is relatively low (3–5 MPa·m¹⁄²). Under extremely high-speed collisions or hard impacts, there is a risk of breakage. Optimize rotational speed and ball charge to avoid excessive inter-ball impact.
Manufactured according to Chinese national standards (GB/T 2480-2022, GB/T 23538-2023) and international standards including ASTM C1327 for Vickers hardness testing.
Core Quality Parameters:
- Wear performance: specific energy wear ≤0.5 g/(kW·h)
- Mechanical properties: Rockwell hardness HRA ≥85
- Size & shape: diameter deviation ±5%; roundness ≥0.9
- Stability: hardness retention rate ≥95% after immersion
Miss. Scarlett.S
Deputy Director of Foreign Trade Department
- メールアドレス: scarlett.s@kegugroup.com
- Tel: 8616602956098
- ワットスアップ: 8613390790728
-
ウェチャット:
Scarlettseren533
-
シリコンカービッド密封リング 1650°C 最大使用温度,380MPa 屈曲強度,耐腐蝕性
シリコンカービッド (SiC) のシールリング 要求の高いアプリケーションのための高度なパフォーマンス 製品概要 圧力をかけないシリコンカービッドシールリングは 密封技術の頂点です 極端な操作条件下で 卓越した性能を 提供するために設計されています小型リングの乾圧,大型部品の同静圧圧を含む先進的な製造プロセスを利用する精密なシールソリューションを 提供します 主要 な 特徴 と 利点 特殊な耐久性高度な硬さと優れた耐磨性を組み合わせて,使用期間を延長し,従来の密封材料を大幅に上回る 全面的な耐腐食性:様々な産業環境で攻撃的な化学物質,酸,腐食媒介にさらされたときに完全性を維持する 優れた熱性能... -
1650℃の最高使用温度、燃料20%削減、耐熱衝撃性を備えたカスタマイズされた炭化ケイ素セラミックパイプバーナー
カスタマイズされたシリコンカービッドセラミックパイプバーナー ZG工業は高性能の シリコンカービッドセラミックパイプバーナーと 極限条件のために設計された 翼付き放射管を 製造しています私たちのSi/SiC複合管は,優れた熱伝達を提供します産業用暖房用には,例外的な耐久性とエネルギー削減が可能です.直径6インチまでのシステムに即座に設置できます. 主要 な 特徴 と 利点 優れた材料特性:2450°F (1343°C) まで高温耐性のある優れた耐磨性,酸化性,腐食性 熱の移転が強化される熱効率と配分を向上させるため,先端な翼管設計により表面面積が増加する 証明されたエネルギー節約:熱性能を維持... -
優れた耐摩耗性、長寿命、精密工学を特徴とする炭化ケイ素サンドブラストノズル。産業用途向け。
シリコンカービッド (SiC) の砂吹きノズル 工業用表面処理用には優れた耐磨性 シリコンカービッド砂吹きノズルは 表面処理の要求の高いアプリケーションで 耐久性と精度を極めるように設計されています先進的なイソスタティックプレスと圧力なしのシンタリング技術で製造精密な掘削,溝付け,複雑な曲線を含むすべての表面の仕上げを,正確な操作要件を満たすために. 主要 な 特徴 と 利点 特殊な耐磨性:超高密度 (>3.15 g/cm3) とビッカース硬度 (≥23 GPa) を備えて,磨き環境における最大使用寿命を保証する 精密エンジニアリング一貫した,信頼性の高いパフォーマンスのために,0.01mmま... -
NIJ認定 シリコンカービッド体甲 複数打撃能力と軽量弾道防御
シリコン カービッド セラミック 装甲: 優れた弾道 防護 私たちの先進的なシリコンカービッド (SiC) セラミック装甲は,特殊な硬さ (9.5 モース) と著しく減重して,高速や装甲穿刺の脅威に対して,人員や車両に比類のない保護を提供. 弾道 技術の 主要 な 利点 複数のヒット能力:連続した影響下で構造的整合性を維持し,ダイナミックな任務における信頼性を確保する 軽量防衛同等の保護レベルで鋼鉄装甲より最大70%軽く,着用者の疲労を軽減し,移動性を高めます NIJ標準の完全遵守:保護レベルIからIVまでの独立認証された性能 カスタマイズできる幾何学:方形,六角形,円筒形,その他の配置で利用...